Unknown · ABS · by super-system · 0 downloads

Download for Bambu Studio Download for OrcaSlicer Download for PrusaSlicer

Compare

Inheritance

*common*

→

*BasicABS*

→

*kvpABS*

Inherited from this (2)

Settings

Basic information

Material variant: ABS inherited
Diameter (mm): 1.75 inherited
Density (g/cm³): 1.05 overridden
was 1.04 (inherited)
Cost (/kg): 22 overridden
was 20 (inherited)

Print temperature

Nozzle (initial layer) (°C): 240 overridden
was 250 (inherited)
Nozzle (other layers) (°C): 235 overridden
was 250 (inherited)
Chamber (°C): 50 inherited

Cooling

Fan minimum (%): 15 overridden
was 0 (inherited)
Fan maximum (%): 30 overridden
was 0 (inherited)
Disable fan for first N layers: 5 overridden
was 3 (inherited)
Full fan if layer below (sec): 45 overridden
was 20 (inherited)
Slow down if layer below (sec): 15 inherited
Min speed when slowed (mm/s): 15 inherited

Flow

Flow ratio: 1 inherited

Bed temperature

Plate	Initial layer (°C)	Other layers (°C)
High Temp Plate	110 overridden was 100	105 overridden was 90

Other settings

bridge fan speed: 30 overridden
was 30 (inherited)
cooling: 1 overridden
was 0 (inherited)
fan always on: 1 overridden
was 0 (inherited)
filament colour: #FFFF00 overridden
was #3A80CA (inherited)
filament cooling final speed: 3.4 inherited
filament cooling initial speed: 2.2 inherited
filament cooling moves: 4 inherited
filament load time: 0 inherited
filament loading speed: 28 inherited
filament loading speed start: 3 inherited
filament minimal purge on wipe tower: 15 inherited
filament ramming parameters: 120 100 6.6 6.8 7.2 7.6 7.9 8.2 8.7 9.4 9.9 10.0| 0.05 6.6 0.45 6.8 0.95 7.8 1.45 8.3 1.95 9.7 2.45 10 2.95 7.6 3.45 7.6 3.95 7.6 4.45 7.6 4.95 7.6 overridden
was 120 100 5.70968 6.03226 7 8.25806 9 9.19355 9.3871 9.77419 10.129 10.3226 10.4516 10.5161| 0.05 5.69677 0.45 6.15484 0.95 8.76774 1.45 9.20323 1.95 9.95806 2.45 10.3871 2.95 10.5677 3.45 7.6 3.95 7.6 4.45 7.6 4.95 7.6 (inherited)
filament soluble: 0 inherited
filament toolchange delay: 0 inherited
filament unload time: 0 inherited
filament unloading speed: 90 inherited
filament unloading speed start: 100 inherited
top fan speed: 30 overridden

Raw resolved JSON

{
  "cooling": [
    "1"
  ],
  "filament_cost": [
    "22"
  ],
  "filament_notes": [
    ""
  ],
  "filament_density": [
    "1.05"
  ],
  "filament_soluble": [
    "0"
  ],
  "filament_diameter": [
    "1.75"
  ],
  "end_filament_gcode": [
    ""
  ],
  "filament_load_time": [
    "0"
  ],
  "compatible_printers": [
    ""
  ],
  "filament_flow_ratio": [
    "1"
  ],
  "slow_down_min_speed": [
    "15"
  ],
  "filament_settings_id": [
    ""
  ],
  "filament_unload_time": [
    "0"
  ],
  "slow_down_layer_time": [
    "15"
  ],
  "start_filament_gcode": [
    ""
  ],
  "filament_cooling_moves": [
    "4"
  ],
  "filament_loading_speed": [
    "28"
  ],
  "filament_unloading_speed": [
    "90"
  ],
  "filament_toolchange_delay": [
    "0"
  ],
  "filament_ramming_parameters": [
    "120 100 6.6 6.8 7.2 7.6 7.9 8.2 8.7 9.4 9.9 10.0| 0.05 6.6 0.45 6.8 0.95 7.8 1.45 8.3 1.95 9.7 2.45 10 2.95 7.6 3.45 7.6 3.95 7.6 4.45 7.6 4.95 7.6"
  ],
  "filament_cooling_final_speed": [
    "3.4"
  ],
  "filament_loading_speed_start": [
    "3"
  ],
  "compatible_printers_condition": [
    ""
  ],
  "filament_cooling_initial_speed": [
    "2.2"
  ],
  "filament_unloading_speed_start": [
    "100"
  ],
  "filament_minimal_purge_on_wipe_tower": [
    "15"
  ],
  "fan_always_on": [
    "1"
  ],
  "fan_max_speed": [
    "30"
  ],
  "fan_min_speed": [
    "15"
  ],
  "filament_type": [
    "ABS"
  ],
  "hot_plate_temp": [
    "105"
  ],
  "filament_colour": [
    "#FFFF00"
  ],
  "bridge_fan_speed": [
    "30"
  ],
  "nozzle_temperature": [
    "235"
  ],
  "chamber_temperature": [
    "50"
  ],
  "fan_cooling_layer_time": [
    "45"
  ],
  "close_fan_the_first_x_layers": [
    "5"
  ],
  "hot_plate_temp_initial_layer": [
    "110"
  ],
  "nozzle_temperature_initial_layer": [
    "240"
  ],
  "top_fan_speed": [
    "30"
  ],
  "name": "*kvpABS*",
  "type": "filament"
}